特点：LNP VERTON PA66 RV007ES compound 是一款含35%长玻璃纤维和热稳定,易于成型的尼龙66材料.
PA66 RV007ES compound 含长玻纤,热稳定
LNP? VERTON? PA66 RV007ES compound
聚酰胺66
35%长玻璃纤维
SABIC Innovative Plastics (Americas)
产品说明
Also known as:LNP? VERTON? Compound RF-7007 EM HS
Product reorder name:RV007ES
LNP VERTON* RV007ES is a compound based on Nylon 66 resin containing 35% Long Glass Fiber. Added features of this material include: Easy Molding, Heat Stabilized, Structural.
增强填料：含35%长玻璃纤维
材料特点：热稳定,易于成型
塑料牌号：PA66 RV007ES
定属记号：尼龙66
加工方法：注射成型
销售电话：13826985763马经理
 
材料物性
MECHANICAL
Value
Unit
Standard
Tensile Stress,break
2080
kgf/cm?
ASTM D 638
Flexural Modulus
100700
kgf/cm?
ASTM D 790
Tensile Stress,break
214
MPa
ISO 527
Tensile Strain,break
2.1
%
ISO 527
Tensile Modulus,1 mm/min
11970
MPa
ISO 527
Flexural Stress
309
MPa
ISO 178
Flexural Modulus
10240
MPa
ISO 178
IMPACT
Value
Unit
Standard
Izod Impact,notched,23℃
28
cm-kgf/cm
ASTM D 256
Izod Impact,notched 80*10*4  23℃
29
kJ/m?
ISO 180/1A
Izod Impact,notched 80*10*4 -40℃
25
kJ/m?
ISO 180/1A
THERMAL
Value
Unit
Standard
HDT,1.82 MPa,3.2mm,unannealed
245
℃
ASTM D 648
HDT/Af,1.8 MPa Flatw 80*10*4   sp=64mm
252
℃
ISO 75/Af
PHYSICAL
Value
Unit
Standard
Density
1.42
g/cm?
ASTM D 792
Moisture Absorption,50% RH,24 hrs
0.97
%
ASTM D 570
Density
1.42
g/cm?
ISO 1183
Injection Molding
Value
Unit
Drying Temperature
80
℃
Drying Time
4
hrs
Maximum Moisture Content
0.15-0.25
%
Melt Temperature
290-305
℃
Front-Zone 3 Temperature
290-300
℃
Middle-Zone 2 Temperature
290-300
℃
Rear-Zone 1 Temperature
280-295
℃
Mold Temperature
95-110
℃
Back Pressure
0.2-0.3
MPa
Screw Speed
30-60
rpm
PA66 LNP? VERTON? COMPOUND
Crystalline polyamide 6,6 is one of the most widely used engineering plastics, combining easy processing with high impact strength, excellent thermal performance, and good economics. Provides good paintability and can be modified with tougheners and internal lubricants.